Potential of secondary aerosol formation from Chinese gasoline engine exhaust

Light-duty gasoline vehicles have drawn public attention in China due to their significant primary emissions of particulate matter and volatile organic compounds(VOCs). However,little information on secondary aerosol formation from exhaust for Chinese vehicles and fuel conditions is available. In this study, chamber experiments were conducted to quantify the potential of secondary aerosol formation from the exhaust of a port fuel injection gasoline engine. The engine and fuel used are common in the Chinese market, and the fuel satisfies the China V gasoline fuel standard. Substantial secondary aerosol formation was observed during a 4–5 hr simulation, which was estimated to represent more than 10 days of equivalent atmospheric photo-oxidation in Beijing. As a consequence, the extreme case secondary organic aerosol(SOA) production was 426 ± 85 mg/kg-fuel, with high levels of precursors and OH exposure. The low hygroscopicity of the aerosols formed inside the chamber suggests that SOA was the dominant chemical composition. Fourteen percent of SOA measured in the chamber experiments could be explained through the oxidation of speciated single-ring aromatics. Unspeciated precursors, such as intermediate-volatility organic compounds and semi-volatile organic compounds, might be significant for SOA formation from gasoline VOCs. We concluded that reductions of emissions of aerosol precursor gases from vehicles are essential to mediate pollution in China.     

Nanoencapsulation of hexavalent chromium with nanoscale zero-valent iron: High resolution chemical mapping of the passivation layer

Solid phase reactions of Cr(Ⅵ) with Fe(0) were investigated with spherical-aberration-corrected scanning transmission electron microscopy(Cs-STEM) integrated with X-ray energy-dispersive spectroscopy(XEDS). Near-atomic resolution elemental mappings of Cr(Ⅵ)–Fe(0) reactions were acquired. Experimental results show that rate and extent of Cr(Ⅵ) encapsulation are strongly dependent on the initial concentration of Cr(Ⅵ) in solution. Low Cr loading in nZⅥ(1.0 wt%) promotes the electrochemical oxidation and continuous corrosion of n ZⅥ while high Cr loading(1.0 wt%) can quickly shut down the Cr uptake. With the progress of iron oxidation and dissolution, elements of Cr and O counter-diffuse into the nanoparticles and accumulate in the core region at low levels of Cr(Ⅵ)(e.g., 10 mg/L). Whereas the reacted n ZⅥ is quickly coated with a newly-formed layer of 2–4 nm in the presence of concentrated Cr(Ⅵ)(e.g., 100 mg/L). The passivation structure is stable over a wide range of pH unless pH is low enough to dissolve the passivation layer. X-ray photoelectron spectroscopy(XPS) depth profiling reconfirms that the composition of the newly-formed surface layer consists of Fe(Ⅲ)–Cr(Ⅲ)(oxy)hydroxides with Cr(Ⅵ) adsorbed on the outside surface. The insoluble and insulating Fe(Ⅲ)–Cr(Ⅲ)(oxy)hydroxide layer can completely cover the n ZⅥ surface above the critical Cr loading and shield the electron transfer. Thus, the fast passivation of nZⅥ in high Cr(Ⅵ) solution is detrimental to the performance of nZⅥ for Cr(Ⅵ) treatment and remediation.     

Effect of TiO2 nanoparticle aggregation on marine microalgae Isochrysis galbana

TiO_2 nanoparticles(NPs) could adversely impact aquatic ecosystems. However, the aggregation of these NPs could attenuate this effect. In this work, the biological effects of TiO_2 NPs on a marine microalgae Isochrysis galbana were investigated. The aggregation kinetics of TiO_2 NPs under different conditions was also investigated to determine and understand these effects. Results showed that, though TiO_2 NPs had no obvious impact on the size and reproducibility of algal cells under testing conditions, they caused a negative effect on algal chlorophyll, which led to a reduction in photosynthesis. Furthermore, fast aggregation of TiO_2 NPs occurred under all conditions, especially at the pH close to the p Hzpc. Increasing ionic strength and NP concentration also enhanced the aggregation rate.The aggregation and the following sedimentation of TiO_2 NPs reduced their adverse effects on I. galbana.     

Long-term effects of sliver nanoparticles on the abundance and activity of soil microbiome

正Silver nanoparticles(Ag NPs)are among the most extensively used engineered nanomaterials because of their wellestablished antimicrobial and unique physicochemical properties(Yin et al.,2015).Applications of AgNPs have now been     

Seasonal variation and size distribution of biogenic secondary organic aerosols at urban and continental background sites of China

Size-resolved biogenic secondary organic aerosols(BSOA) derived from isoprene and monoterpene photooxidation in Qinghai Lake, Tibetan Plateau(a continental background site) and five cities of China were measured using gas chromatography/mass spectrometry(GC/MS). Concentrations of the determined BSOA are higher in the cities than in the background and are also higher in summer than in winter. Moreover, strong positive correlations(R2= 0.44–0.90) between BSOA and sulfate were found at the six sites,suggesting that anthropogenic pollution(i.e., sulfate) could enhance SOA formation,because sulfate provides a surface favorable for acid-catalyzed formation of BSOA. Size distribution measurements showed that most of the determined SOA tracers are enriched in the fine mode( 3.3 μm) except for cis-pinic and cis-pinonic acids, both presented a comparable mass in the fine and coarse( 3.3 μm) modes, respectively. Mass ratio of oxidation products derived from isoprene to those from monoterpene in the five urban regions during summer are much less than those in Qinghai Lake region. In addition, in the five urban regions relative abundances of monoterpene oxidation products to SOA are much higher than those of isoprene. Such phenomena suggest that BSOA derived from monoterpenes are more abundant than those from isoprene in Chinese urban areas.     

海水中阴极极化对X80钢应力腐蚀及氢脆敏感性的影响

目的研究不同p H值海水中阴极极化对X80管线钢应力腐蚀及氢脆的抑制作用。方法采用慢应变速率拉伸试验、电化学测试、微观组织观察等分析方法。结果 X80钢在天然海水中的析氢电位约为-940m V(vs.SCE,下同),海水p H为3.5时析氢电位发生正移。其应力腐蚀敏感性与极化电位有很大关系,随着极化电位负移,X80钢的氢脆敏感性增加。天然海水中当极化电位负于-950 m V时,断口出现准解理断裂特征形貌。在-1050 m V极化电位下,钢材进入氢脆断裂区发生脆性断裂。海水p H为3.5时,-900 m V钢材有发生氢脆的危险。结论与天然海水相比,X80钢在p H为3.5的酸性海水中具有较高的应力腐蚀敏感性,两种海水介质中X80钢的应力腐蚀敏感性均随极化电位负移而增加。     

包装箱用碳纤维增强复合材料贮存寿命研究

目的研究碳纤维增强复合材料贮存条件下的性能变化趋势和寿命评估。方法对碳纤维增强复合材料开展四个不同温度条件下的热氧老化试验,按试验周期定期取样开展冲击性能测试,对试验数据采用寿命预估方法进行处理,对材料性能进行预估。结果通过数据计算分别得到我国热带海洋、干热沙漠等典型气候条件下的碳纤维增强复合材料贮存寿命分别为17.21~35.89年。结论碳纤维增强复合材料具有较好的贮存性能,在较为严酷的热带海洋气候和给定的失效判据条件下,寿命预计为17.21年。试验和数据处理方法可以较好地预计材料的性能变化趋势和开展寿命评估。     

复合型道路抑尘剂在城市道路中的应用及经济分析研究

采用由多种可降解高分子材料组成的新型复合型道路抑尘剂喷洒酒泉市肃州区道路,研究喷洒前后城市道路扬尘中PM_(10)、PM_(2.5)和氮氧化物的变化及抑尘剂所带来的经济效益。结果表明,PM_(10)平均去除率为20%,喷洒后能迅速捕捉并吸附微粒粉尘,加速粉尘颗粒凝聚,最好去除效果高达40%;对PM_(2.5)和氮氧化物的去除效果约15%,没有PM_(10)显著;相对于传统洒水方式,喷洒道路抑尘剂可以节省30%经济用水,且对人体和环境无毒害。     

基层卫生医疗机构财务管理战略对环境污染的影响分析研究

基层卫生医疗机构财务的优化管理能降低环境污染,定量分析基层卫生医疗机构财务管理战略对环境污染的影响,优化基层医疗机构的财务管理水平,从而抑制环境污染,提出基于关联规则统计分析模型的基层卫生医疗机构财务管理模型。结合定量回归分析方法进行环境污染的影响因素分析,采用解释变量的相关性分析方法进行统计平均检验,构建检测统计量和判决统计量进行环境污染影响及医疗卫生结构财务管理的关联规则分析评估,提高基层医疗结构财务管理的智能化水平。